Tianjin Bohai Metal Corporation

410HT Stainless Steel Sheet

Alloy 410 HT is the basic, general purpose, heat treated version of Type 410. It is a martensitic type, used for general purpose, where corrosion is not severe. Alloy 410 contains a minimum of 11.5% chromium which is just sufficient enough to demonstrate corrosion resistance properties in mild atmospheres, steam, and many mild chemical environments.

Stainless Steel Coil/Sheet

Get a price

hiddenValue

Product Detail
| Technical Information
| Packaging

Commodity name: 410HT Stainless Steel Sheet

Product Information

Product Details

Chemical Properties:

	C	Mn	Si	P	S	Cr	Ni
410HT	0.15 max	1.00 max	1.00 max	0.04 max	0.03 max	min: 11.5 max: 13.5	0.50 max

Mechanical Properties:

Grade	Tensile Strength ksi (MPa) min	Yield Strength 0.2% offset ksi (MPa) min	Elongation (% in 50mm) min	Hardness (Brinell) MAX	Hardness (Rockwell B) MAX
410HT	65 (450)	30 (205)	20

Standards:

ASTM/ASME: UNS S41000
EURONORM: FeMi35Cr20Cu4Mo2
DIN: 2.4660

Corrosion Resistance:

Good corrosion resistance to atmospheric corrosion, potable water, and to mildly corrosive environments
Its exposure to everyday activities (sports, food preparation) is generally satisfactory when proper cleaning is performed after exposure to use
Good corrosion resistance to low concentrations of mild organic and mineral acids

Welding Characteristics

Readily welded by all standard methods
To reduce the risk of cracking, it is suggested to pre-heat the work piece to 350 to 400oF (177 to 204oC)
Post weld annealing is recommended to retain maximum ductility

Heat Treatment

The proper hot work range is 2000 to 2200oF (1093 to 1204oC)
Do not work this material below 1650oF (899oC)

Mechanical Properties of Heat Treated 410:

Heat Treatment	T410 (0.14%C) Hardened 1800°F (982°C)
Heat Treatment	Rockwell Hardness	0.2% YS, Ksi (MPa)	UTS, Ksi (MPa)
Annealed*	81 HRB	45.4 (313)	80.4 (554)
Hardened & Tempered 400°F (204°C)	43 HRC	156.1 (1076)	202.9 (1399)
Hardened & Tempered 550°F (288°C)	40 HRC	148.3 (1022)	187.0 (1289)
Hardened & Tempered 600°F (316°C)	40 HRC	148.8 (1026)	186.1 (1283)
Hardened & Tempered 800°F (427°C)	41 HRC	132.9 (916)	188.5 (1300)
Hardened & Tempered 900°F (482°C)	41 HRC	122.6 (845)	154.3 (1063)
Hardened & Tempered 1000°F (538°C)	35 HRC	127.9 (882)	154.3 (1063)
Hardened & Tempered 1200°F (649°C)	98 HRB	85.5 (589)	111.2 (767)

Applications:

Applications requiring moderate corrosion resistance and high mechanical properties are ideal for Alloy 410HT. Examples of applications that frequently used Alloy 410HT include: