- Commodity name: 65Mn hot rolled steel round bars
65Mn high carbon steel is mainly used in the manufacture of various small-section flat springs, round springs, clockwork, etc. It can also be used to manufacture spring rings, valve springs, shock absorbers, clutch reeds and brake springs.
65Mn hot rolled steel round bars information
65Mn steel is a Chinese GB standard spring steel grade, Manganese (Mn) improves hardenability, so the strength, hardness, elasticity and hardenability are higher than that of 65# steel, but it has overheat sensitivity and temper brittleness. Water quenching tends to form cracks. The annealed state has good machinability, low cold deformation plasticity, and poor weldability.
65Mn high carbon steel is mainly used in the manufacture of various small-section flat springs, round springs, clockwork, etc. It can also be used to manufacture spring rings, valve springs, shock absorbers, clutch reeds and brake springs.Chemical and Mechanical
Chemical Composition
The table below lists 65Mn high carbon steel chemical composition based on heat analysis.
Chemical Composition, % Standard Grade C Si Mn P, ≤ S, ≤ Cr, ≤ Ni, ≤ Cu, ≤ GB/T 1222 65Mn 0.62-0.70 0.17-0.37 0.90-1.20 0.030 0.030 0.25 0.35 0.25 65Mn Material Properties
Density: 7.85 g/cm3
Mechanical Properties Standard Grade Tensile Strength, MPa, ≥ Yield Strength, MPa, ≥ Elongation, %, ≥ Reduction in Area, %, ≥ Brinell Hardness, HBW, ≤ GB/T 1222 65Mn 980 785 8.0 30 302 Notes: Bars with a diameter and side length of not more than 80 mm and flat steels with a thickness of not more than 40 mm.
Heat Treatment Specification
Heat Treatment Standard Grade Quenching temperature, °C Quenching medium Tempering temperature, °C GB/T 1222 65Mn 830 ± 20 Oil 540 ± 20 Annealing process: Annealing temperature (860 ± 10) °C, heat preservation for 45-60min, furnace cooling to (750 ± 10) °C, heat preservation for 3-3.5h, and furnace cooling to 650-660 °C, then cooling out of the furnace or slow cooling in a heat preservation pit.
Products & Service
Related Products
Get a Free Quote
To: Tianjin Bohai Metal Company
Tianjin Bohai Metal
Tel : +86 0635 6666186
Fax :+86 0635 6666186
E-mail : bhteddy@cnbhgt.com
E-mail : bhtina@cnbhgt.com
E-mail : bholia@cnbhgt.com
Add : Dongchangfu District, Liaocheng City, Shandong Province