20CrMnTi(H) hot rolled steel round bars
20CrMnTi(H) hot rolled steel round bars
hiddenValue
- Product Detail
- | Technical Information
- | Packaging
-
- Commodity name: 20CrMnTi(H) hot rolled steel round bars
GB 20CrMnTi gear steel is GB standard Alloy Carburizing Gearing steel, GB 20CrMnTi properties is a chromium, manganese, titanium alloy steel specification. 20CrMnTi is equivalent with others standard bearing/Gearing steel, gearing steel
Product introduction
characteristics of hardened steel alloy tool steel, good carburizing heat treatment process and the performance of the steel at ≤960 ℃ fine grain structure, commonly used in long-term heating carburizing temperature, the grain grew no tendency little residual austenite after quenching, therefore, the steel has high strength and wear resistance, excellent cutting performance, the main performance and 20CrMnTi and 20CrNi steel similar. Tensile strength σ ≥1080MPa, yield strength σ ≥885MPa, elongation δ ≥10%, 45% reduction of swelling, impact toughness (impact toughness) α ≥69J / cm, hardness ≤207HB, blank sample size to 15mm.
Technical data
GB 20CrMnTi GB/T 3077 Mechanical
The mechanical properties of GB 20CrMnTi GB/T 3077 metals determine the range of usefulness of a material and establish the service life that can be expected. Mechanical properties are also used to help classify and identify material.
Yield
Rp0.2 (MPa)Tensile
Rm (MPa)Impact
KV/Ku (J)Elongation
A (%)Reduction in cross section on fracture
Z (%)As-Heat-Treated Condition Brinell hardness (HBW) 912 (≥) 863 (≥) 23 33 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 212 Physical performance parameters of GB 20CrMnTi GB/T 3077 are mainly indicated by density, poisson's ratio, thermal conductivity, specific thermal capacity, coefficient of thermal expansion, modulus of elasticity, electrical resistance value, etc.
Temperature
(°C)Modulus of elasticity
(GPa)Mean coefficient of thermal expansion 10-6/(°C)
between 20(°C) andThermal conductivity
(W/m·°C)Specific thermal capacity
(J/kg·°C)Specific electrical resistivity
(Ω mm²/m)Density
(kg/dm³)Poisson’s coefficient, ν 24 - - 0.31 - 956 121 - 12.3 423 - 659 - 41 11.2 243 423 Heat treatment Related
- Annealing of 20CrMnTi Alloy Gearing steel
Slowly heated to 790-810 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. Different annealing ways will get different hardness.The 20CrMnTi Gearing steel will get Hardness MAX 248 HB （Brinell hardness）.
- Quenching and temperature of 20CrMnTi gear steel
Heated slowly to 788°C, Then put in salt-bath furnace keep 1191 ℃to 1204 ℃。quenching by oil get 60 to 66 HRc hardness. High temperature tempering: 650-700℃，cool in air, get hardness 22 to 30HRC. Low temperature tempering: 150-200 ℃， Cool in ari, get 61-66HRC hardness.
- Hot work and cold work of 20CrMnTi Alloy Gearing steel
GB 20CrMnTi steel can hot worked at 205 to 538°C, 20CrMnTi Bearing/Gearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.
Products & Service
Related Products
Get a Free Quote
To: Tianjin Bohai Metal Company
Tianjin Bohai Metal
Tel : +86 0635 6666186
Fax :+86 0635 6666186
E-mail : bhteddy@cnbhgt.com
E-mail : bhtina@cnbhgt.com
E-mail : bholia@cnbhgt.com
Add : Dongchangfu District, Liaocheng City, Shandong Province