20CrMo hot rolled steel sheet

20crmo Alloy Steel Bar is widely used to manufacture pressure tube and fastener which is non-corrosive medium, nitrogen hidrogen medium and work under 250°C, such as vane, baffle, forging and rolled section in turbine and boiler, important carburing parts in common machine.

Steel Round Bars

Get a price

hiddenValue

Product Detail
| Technical Information
| Packaging

Commodity name: 20CrMo hot rolled steel sheet

Product introduction

steel round bars are widely used in machinery making, autombile making, railway, mine machinery, petoleum machinry, agricultural machinery and civil archtectue such as all kinds of shafts, screws, connecting rods, hardware tools, gears, standard parts, spanners fasteners, structural parts for automobile and agricultural machinery, outer and iner sleeves, rollers and balls for bearing making.
GB 20CrMo steel is a kind of Chinese alloy steel for engineering and mechanical structure purpose, which is generally used in quenching or tempering or carburizing and quenching. 20CrMo material has high heat strength, good hardenability, no temper brittleness, cold strain plasticity, good machinability and weldability.

Technical data

20crmo Alloy Steel Bar Chemical Composition

Grade	C	Si	Mn	P	S	Cr	Mo
20CrMo	0.17-0.24	0.17-0.37	0.40-0.70	≤0.030	≤0.030	0.80-1.10	0.15-0.25

Mechanical Property:

Tensile strength σb (MPa)	Yield Strength σs 0.2 (MPa)	Elongation δ 5 (%)	Reduction of crosssection area ψ (%)	Ballistic work Akv (J)	Pounding toughness value αkv (J/cm2)	Hardness (HB)	Specimen Size
Min 835	Min 540	Min 10	Min 40	Min 47	Min 59	Max 179	15mm

Applications

20CrMo alloy steel is used in the manufacture of non-corrosive media in chemical equipment and high pressure pipes, fasteners, steam turbines, boiler blades and forgings with working temperature below 250 °C, and important carburizing parts such as gears and shafts in general machines. It can also be used in place of 1Cr13 steel to manufacture medium pressure, low pressure steam turbines in the superheated steam zone pressure stage working blades.