Stainless steel 430 is a non-hardenable steel containing straight chromium, and belongs to the ferritic group of steels.
Product introduction
Stainless steel 430 is a non-hardenable steel containing straight chromium, and belongs to the ferritic group of steels. This steel is known for its good corrosion resistance and formability, coupled with practical mechanical properties. It can be used in certain chemical applications due to its resistance to nitric acid.
430F stainless steel is usually provided in bar form to be used in automatic screw machines. factory Standard AISI ASTM hot/cold roll stainless steel plateTechnical data
Chemical Composition
GradeN C Mn Si P S Cr Mo Ni N 430 min.
max.-
0.12-
1-
1-
0.04-
0.03016
18- -
0.50- 430F min.
max.-
0.12-
1.25-
1-
0.060.15
-16
18- - -
Mechanical PropertiesGrade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness Rockwell B (HR B) max Brinell (HB) max 430 483 310 22 85 183 430F 552 typical 379 typical 25 typical - 262
Physical PropertiesGrade Density (kg/m3) Elastic Modulus (GPa) Mean Coefficient of Thermal Expansion
(μm/m/°C)Thermal Conductivity
(W/m.K)Specific Heat 0-100°C (J/kg.K) Electrical Resistivity (nΩ.m) 0-100°C 0-315°C 0-538°C at 100°C at 500°C 430 7750 200 10.4 11.0 11.4 26.1 26.3 460 600 430F 7750 200 10.4 11.0 11.4 26.1 26.3 460 600
Grade Specification ComparisonGrade UNS No Old British Euronorm Swedish SS Japanese JIS BS En No Name 430 S43000 430S17 60 1.4016 X8Cr17 2320 SUS 430 430F S43020 - - 1.4104 X12CrMoS17 2383 SUS 430F
Possible Alternative GradesGrade Reasons for choosing 430 430F Higher machinability than 430 is needed in bar product, and reduced corrosion resistance is acceptable 434 Better pitting resistance is required 304 Slightly higher corrosion resistance is needed, together with greatly improved ability to be welded and cold formed 316 Much better corrosion resistance is needed, coupled with greatly improved ability to be welded and cold formed 3CR12 Lower corrosion resistance is acceptable in a cost-critical application
Key words:- Stainless steel 430
- 430F
Products & Service
Related Products
Get a Free Quote
To: Tianjin Bohai Metal Company
Tianjin Bohai Metal
Tel : +86 0635 6666186
Fax :+86 0635 6666186
E-mail : bhteddy@cnbhgt.com
E-mail : bhtina@cnbhgt.com
E-mail : bholia@cnbhgt.com
Add : Dongchangfu District, Liaocheng City, Shandong Province