Alloy 317L (UNS S31703) is a molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless steels such as Alloy 304. In addition, Alloy 317L offers higher creep, stress-to-rupture, and tensile strength at elevated temperatures than conventional stainless steels. It is a low carbon or "L" grade which provides resistance to sensitization during welding and other thermal processes.

图片名称

hiddenValue

  • Product Detail
  • | Technical Information
  • | Packaging
    • Commodity name: 317L Stainless Steel

    Alloy 317L (UNS S31703) is a molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless steels such as Alloy 304. In addition, Alloy 317L offers higher creep, stress-to-rupture, and tensile strength at elevated temperatures than conventional stainless steels. It is a low carbon or "L" grade which provides resistance to sensitization during welding and other thermal processes.

    Product information

    General Properties
    Alloy 317L (UNS S31703) is a lowcarbon corrosion resistant austenitic chromium-nickel-molybdenum stainless steel. The high levels of these elements assure the alloy has superior chloride pitting and general corrosion resistance to the conventional 304/304L and 316/316L grades. The alloy provides improved resistance relative to 316L in strongly corrosive environments containing sulfurous media, chlorides, and other halides.

    The low carbon content of Alloy 317L enables it to be welded without intergranular corrosion resulting from chromium carbide precipitation enabling it to be used in the as-welded condition. With the addition of nitrogen as a strengthening agent, the alloy can be dual certified as Alloy 317 (UNS S31700).

    Alloy 317L is non-magnetic in the annealed condition. It cannot be hardened by heat treatment, however the material will harden due to cold working. Alloy 317L can be easily welded and processed by standard shop fabrication practices.
     

    Standard: ASTM A240,ASME SA240,AMS 5524/5507
    Thickness:  0.3 ~ 12.0mm
    Width Range:  4'*8ft',4'*10ft',1000*2000mm,1500x3000mm etc
    Brand name: TISCO,  ZPSS, BAOSTEEL, JISCO 
    Technique:  Cold Rolled ,Hot rolled
     Forms :

    Foils, Shim Sheet, Rolls, Perforated Sheet, Chequered Plate.

     Applications  Pulp and Paper  Textiles  Water Treatment

     

    Technical data

    ALLOY Composition (Weight Percent) PREN1
    Cr Mo N
    304 Stainless Steel 18.0 0.06 19.0
    316 Stainless Steel 16.5 2.1 0.05 24.2
    317L Stainless Steel 18.5 3.1 0.06 29.7
    SSC-6MO 20.5 6.2 0.22 44.5

    Chemical Analysis

    Weight % (all values are maximum unless a range is otherwise indicated)

    Chromium 18.0 min.-20.0 max. Phosphorus 0.045
    Nickel 11.0 min.-15.0 max. Sulfur 0.030
    Molybdenum 3.0 min. - 4.0 max. Silicon 0.75
    Carbon 0.030 Nitrogen 0.10
    Manganese 2.00 Iron Balance

    Mechanical Properties

    Values at 68°F (20°C) (minimum values, unless specified)

    Yield Strength
    0.2% Offset
    Ultimate Tensile
    Strength
    Elongation
    in 2 in.
    Hardness
    psi (min.) (MPa) psi (min.) (MPa) % (min.) (max.)
    30,000 205 75,000 515 40 95 Rockwell B


     

    Key words:
    • 317L Stainless Steel

Get a Free Quote


To: Tianjin Bohai Metal Company


Action
I would like some more details. Product Requirements: Customization: Delivery Time: Payment: Shipping: Usage:
((Max 5 files. Support jpg, jpeg, png, gif, txt, doc, pdf, xls, docx, xlsx, less than 5MB))

Contact & Optional Details

Send Inquiry Now